ORIGINAL RESEARCH Table of Contents   
Year : 2008  |  Volume : 19  |  Issue : 1  |  Page : 2-5
Effect of chemical surface treatments and repair material on transverse strength of repaired acrylic denture resin


Department of Prosthodontic, Faculty of Dentistry, Shiraz University of Medical Sciences, Shiraz, Iran

Click here for correspondence address and email

Date of Submission25-Nov-2006
Date of Decision30-Mar-2007
Date of Acceptance10-Apr-2007
 

   Abstract 

Purpose: This study was performed to evaluate the transverse strength of a denture base resin (H), repaired with an autopolymerizing acrylic resin (A) or a visible light-curing (VLC) resin (T) following the use of three chemical solvents: methyl methacrylate monomer, aceton or chloroform.
Materials and Methods: Eighty specimens (65.0 10.0 3.3 mm) of H were fabricated and stored in distilled water at 37C for seven days. Specimens were divided into eight equal groups of 10. In each group, specimens were sectioned in the middle to create a 10 mm gap. Two groups served as controls and had no surface treatment. They were repaired with A or T materials. In the remaining six experimental groups, specimen surfaces were treated with ac for 30 sec or mma for 180 sec or ch for 5 sec. Then A or T material was placed on the treated surfaces, using the same preparation molds. After seven days' storage at 37C, the transverse bond strength (MPa) of the specimens was measured using a three-point bending test. A two-way ANOVA and a Tukey HSD were performed to identify significant differences ( P < 0.05). The nature of the failures was noted as adhesive, cohesive or mixed.
Results: Significant differences were found between the controls and experimental groups ( P < 0.05). In the control groups, repair with A showed significantly higher strength (60.3 MPa) than those repaired with T (51.3 MPa). Mean transverse strength of experimental specimens repaired with A was (75.06 MPa) which was significantly greater than those repaired with T (67.9 MPa). Although surface treatment increased repair strength, no significant differences were detected between the effects of the chemical etchants.
Conclusions: The autopolymerizing resin exhibited significantly higher repair strength than VLC resin. The transverse strength of the repaired specimens was increased significantly after chemical treatments.

Keywords: Autopolymerizing resin, surface treatment, transverse strength, VLC resin

How to cite this article:
Vojdani M, Rezaei S, Zareeian L. Effect of chemical surface treatments and repair material on transverse strength of repaired acrylic denture resin. Indian J Dent Res 2008;19:2-5

How to cite this URL:
Vojdani M, Rezaei S, Zareeian L. Effect of chemical surface treatments and repair material on transverse strength of repaired acrylic denture resin. Indian J Dent Res [serial online] 2008 [cited 2014 Sep 3];19:2-5. Available from: http://www.ijdr.in/text.asp?2008/19/1/2/38923
Acrylic resin complete dentures are susceptible to fracture after long periods of clinical use. [1] The repair of fractured prosthesis can be accomplished using acrylic resins that are light polymerized, autopolymerized, heat polymerized or microwave polymerized. [2]

Among these acrylic resins, Triad, which is a visible light-curing (VLC) material and also autopolymerized acrylic resin can be used for chairside repair of dentures. [3] Although the conventional and microwave polymerized materials demonstrate superior strength, these materials require a significant amount of working time due to necessary packing and flasking procedures and also present the added risk of denture distortion by heat. [2],[4]

However, recent developments in processing methods and materials may result in superior strength of autopolymerizing acrylic resins to those previously reported. For example, the use of air pressure and low heat were reported to reduce the porosity of chemically accelerated materials, thus increasing the repair strength. [5]

The suitability of Triad for denture repair was tested by Khan et al . who reported that it was satisfactory in terms of strength. [6] Craig et al . also supported these results since they observed no problems in repairing resins with this material. [5]

Although the physical and mechanical properties of VLC resins were reported well with conventional heat-activated resins, some studies showed lower elastic modules and lower transverse strength for VLC resins, which could increase deformation of dentures during function. [7]

The purpose of this in vitro study was to evaluate the transverse strength of a heat-polymerized acrylic resin, when repaired with an autopolymerizing acrylic resin or a VLC resin following the use of three chemical solvents- methyl methacrylate, aceton or chloroform.


   Materials and Methods Top


The materials used in this study are recorded in [Table - 1]. A heat-curing denture base resin was used to prepare 65.0 10.0 3.3 mm specimens. Eighty heat-polymerized (H) specimens were processed by placing denture resin under compression in 74C water for eight hours in metal flasks. Once processed, all the flasks were bench cooled for 30 min. The specimens were ground with 320-grit silicon carbid paper to remove surface irregularities and excess materials. Afterwards, specimens were stored in water at 37C for seven days before the repair procedures. After storage, the specimens were sectioned in the middle using a double-sided diamond disc. The cut ends of each specimen were ground to 45 bevel joints with 600-grit silicon carbide papers until 10 mm of the total length of the specimens was removed. The surfaces were then ultrasonically cleaned with distilled water and dried with a blast of air. The specimens were divided into eight equal groups, each with 10 specimens [Table - 2].

In two groups (H and G) as controls, without any surface treatment, repair was done with Triad (T) or autopolymerized (A) acrylic resin respectively. In the remaining 60 specimens, the exposed surfaces were treated with chemical etchants, either by immersion in acetone (Ac) for 30 sec, [8] in methyl methacrylate (MMA) for 180 sec [9] or chloroform (Ch) for 5 sec. [10] Once polished and cleaned, the specimens were returned and positioned into the same preparation mold in such a way that a 10-mm gap existed between the two sections of the specimens. For 30 specimens the material A was mixed according to the manufacturer's recommendations and added to the gap in a free-flowing stage. These specimens were processed under two bars in 45C for 15 min.

The remaining 30 specimens were also placed in their mold and the gaps were repaired with T material. The material T was adapted into the gap by finger pressure. They were placed in the light-curing unit for 5 min initially, then removed from the mold and cured for an additional 8 min on the other side. After polymerization, all the specimens were finished to a final dimension of 65.0 10.0 3.3 mm (ISO/FDIS 1567). [11] After the repair procedures, the specimens were stored in distilled water at 37C for seven days. The transverse strength (s) of the controls and repaired specimens was measured using a three-point bending test in a universal testing machine with a 100 kg load cell and a crosshead speed of 5 mm/min.

The transverse strength was determined using the formula: S = 3W1/2bd 2

Where W is the fracture load, l is the distance between supports (25 mm) b is the width and d is the thickness of the specimens. In addition, the nature of failure was noted as adhesive (AD) cohesive (Co) or mixed (MI). Mean values and standard deviations were calculated. Data were analyzed by two-way ANOVA and mean values were compared by using the Tukey (HSD) test (significance level equal 0.05).


   Results Top


The mean transverse strength values and SDs of the groups are presented in [Table - 3]. The 2-way ANOVA in [Table - 4] shows the differences among the groups. The type and frequency of failures for specimens are presented in [Table - 5].

The transverse strength of repaired experimental specimens was significantly greater than the controls ( P -value = 0.000). In the control groups, G showed a significantly higher (60.3 MPa) ( P -value = 0.022) transverse strength than H (51.3 MPa). After surface treatment, all experimental specimens showed higher transverse strength. Significant differences ( P -value = 0.000) were detected between the specimens repaired with A (mean = 75.13) and those repaired with T (mean = 65.96). The specimens repaired with A showed a significantly higher transverse strength than the specimens repaired with T. The mean transverse strength of the examined groups which were repaired with A or T was 75.06 MPa and 67.9 MPa respectively.

The effect of surface treatment of three kinds of chemical etchants on transverse strength showed no significant differences between the experimental groups. However, after chemical etching of cutting surfaces, significant differences were observed between the controls and the experimental specimens ( P -value = 0.000).

The specimens showed three types of failures including adhesive (interface), cohesive (only at repair material) and mixed (interface and repair material ones). Mixed and cohesive fractures were the most common types of failure for the examined groups. However, the controls showed adhesive and mixed failures.


   Discussion Top


The results of this study supported the hypothesis that the chemical and physical properties of acrylic resins, as well as surface treatment affect the bond strength of repair material. The control groups showed significantly lower transverse strength than the experimental groups ( P -value = 0.000). In control groups, repair with A material showed a higher (60.3 MPa) and with T material showed a lower (51.3 MPa) transverse strength value.

Razavi et al. detected that the bond strength of Triad to denture base resin was sufficiently high to suggest its clinical applicability as reline material. [12] Some studies demonstrated that both visible light-cured and heat-cured resin have comparable values for transverse strength and also similar results with regard to their mechanical properties. [6],[13] Lewinstein et al. reported that transverse bond strength of Triad to heat-cured resin did not differ significantly from that of autopolymerized acrylic resin. [14]

In the present study transverse bond strength of T to H was significantly lower than A to H. This finding was supported by the work of Goto et al., [15] Andreopoulos et al . [16] and Dixon et al . [17] too, because of Triad's high viscosity and poor adhesion. However, surface treatment led to stronger repairs.

Andreopoulos et al. indicated that chemical etching with mma was useful to increase the bond strength of Triad. [16]

Lewinstein et al . reported that pretreatment of a denture with either monomer or bonding agent is essential for a stronger bond of Triad VLC reline resin. In this study, the use of monomer rather than bonding agent resulted in a stronger bond. [14] In the present study surface treatment increased the transverse bond strength of both A and T materials but the effect of ac, ch and mma was approximately similar and no significant differences were detected between the experimental groups. Successful denture repair relies on the phenomenon of adhesion. Strong bonding of the surfaces improves the strength of the repaired unit and reduces stress concentration. Adhesion can be improved by first applying appropriate chemicals to the acrylic resin surfaces. [8],[9] These chemicals etch the surface by changing the morphology and chemical properties of the materials. Surface treatments cause superficial crack propagation, as well as the formation of numerous pits approximately 2 mm in diameter. [18] Chemical surface dissolution of acrylic resin could be affected by the degree of cross-linking of the polymer chain. [10] Normally this change is obtained by wetting the surfaces with mma. Organic solvents such as ch, ac and methylen chloride have also been used for this process. [2],[8],[10] Vallitte et al . stated that 180 sec of wetting of polymethacrylate with mma enhanced adhesion, compared with shortened duration of wetting. [9] Shen et al . noticed a duration of 5 sec wetting with chloroform, because longer contact with chloroform undermined the structure of PMMA denture at repair surface. [10]

On acetone, no guidelines were available in the literature concerning the most effective application time of acetone. However, the application time for other chemical treatments was generally stated as 30 sec. [2],[8] The application of aceton to repair surfaces for different time periods should be investigated in the future.

In the present study, the repair joint design was 45 bevel. According to the results of Ward et al . the strength of repairs made with round and 45 bevel joint contour were similar and significantly greater than those with a butt joint design. [19]


   Conclusion Top


We can conclude within the limitation of this study that (1) The specimens repaired with Triad-VLC resin showed significantly lower transverse bond strength than specimens repaired with autopolymerizing acrylic resin, (2) For the denture base resin tested, aceton, MMA and chloroform provided statistically identical bond strength values, (3) The transverse bond strength of repair materials to denture base resin increased significantly with chemical treatments.

 
   References Top

1.Vallittu PK. Glass fiber reinforcement in repaired acrylic resin removable dentures: Preliminary results of a clinical study. Quintessence Int 1997;28:39-44.  Back to cited text no. 1    
2.Rached RN, Powers JM, Del Bel Cury AA. Repair strength of autopolymerizing, microwave and conventional heat-polymerized acrylic resins. J Prosthet Dent 2004;92:79-82.  Back to cited text no. 2    
3.Dar-Odeh NS, Harrison A, Abu-Hammad O. An evaluation of self -cured and visible light-cured denture base materials when used as a denture base repair material. J Oral Rehabil 1997;24:755-60.  Back to cited text no. 3    
4.Dyer RA, Howlett JA. Dimensional stability of denture bases following repair with microwave resin. J Dent 1994;22:236-41.  Back to cited text no. 4    
5.Craig RG, Powers JM. Restorative dental materials. 11 th ed. Elsevier: St. Louis; 2001. p. 665-6.  Back to cited text no. 5    
6.Khan Z, Razavi R, von Fraunhofer JA. The physical properties of a visible light-cured temporary fixed partial denture material. J Prosthet Dent 1988;60:543-5.  Back to cited text no. 6    
7.Zarb GA, Bolender LC. Prosthodontic treatment for edentulous patients. 12 th ed. Elsevier: St. Louis; 2004. p. 194-5.  Back to cited text no. 7    
8.Sinasi YS, Sarac D, Kulunk T, Kulunk S. The effect of chemical surface treatments of different denture base resins on the shear bond strength of denture repair. J Prosthet Dent 2005;94:259-66.  Back to cited text no. 8    
9.Vallittu PK, Lassila P, Lappalainen R. Wetting the repair surface with methyl methacrylate affects the transverse strength of repaired heat-polymerized resin. J Prosthet Dent 1994;72:639-43.  Back to cited text no. 9    
10.Shen C, Colaizzi FA, Birns B. Strength of denture repairs as influenced by surface treatment. J Prosthet Dent 1984;52:844-8.  Back to cited text no. 10    
11.International Organization of Standardization. ISO 1567. Dentistry: Denture base polymers. Geneva, Switzerland: 1998.  Back to cited text no. 11    
12.Razavi R, Khan Z, Fraunhofer JA. The bond strength of a visible light-cured reline resin to acrylic resin denture base material. J Prosthet Dent 1990;63:485-7.  Back to cited text no. 12    
13.Ishigami K, Maeda R, Maeda M, Hamada H, Shou K, Shimada A, et al. Basic studies on visible light- curing resin as a denture base-part 17: Transverse and tensile strengths of repaired denture base resin using a trial repair resin. J Nihon Univ Sch Dent 1993;35:36-42.  Back to cited text no. 13    
14.Lewinstein I, Zeltzer C, Mayer CM, Tal Y. Transverse bond strength of repaired acrylic resin strips and temperature rise of dentures relined with VLC reline resin. J Prosthet Dent 1995;74:392-9.  Back to cited text no. 14    
15.Gotoh H, Umi T, Aoyama Y, Ishizaki T, Umezu N, Ishigami K, et al. A basic study on visible light-cured resins for denture bases- part 1. Nippon Hotetsu Shika Gakki Zasshi 1986;30:387-92.  Back to cited text no. 15    
16.Andreopoulos AG, Polyzois GL, Demetriou PP. Repairs with visible light-curing denture base materials. Quintessence Int 1991;22:703-6.  Back to cited text no. 16    
17.Dixon DL, Eksrand KG, Breeding LC. The transverse strengths of three denture base resins. J Prosthet Dent 1991;66:510-3.  Back to cited text no. 17    
18.Anusavice KJ, Phillips RW. Phillip's science of dental materials. 11 th ed. WB Saunders: Philadelphia; 2003. p. 237-71.  Back to cited text no. 18    
19.Ward JE, Moon PC, Levine RA, Behrendt CL. Effect of repair surface design, repair material and processing method on the transverse strength of repaired acrylic denture resin. J Prosthet Dent 1992;67:815-20.  Back to cited text no. 19    

Top
Correspondence Address:
Mahroo Vojdani
Department of Prosthodontic, Faculty of Dentistry, Shiraz University of Medical Sciences, Shiraz
Iran
Login to access the Email id


DOI: 10.4103/0970-9290.38923

PMID: 18245915

Get Permissions




 
 
    Tables

  [Table - 1], [Table - 2], [Table - 3], [Table - 4], [Table - 5]

This article has been cited by
1 Surface treatment with methyl formate-methyl acetate increased the shear bond strength between reline resins and denture base resin
Rachanee Osathananda,Chairat Wiwatwarrapan
Gerodontology. 2014; : n/a
[Pubmed]
2 Strength comparison of four techniques to secure implant attachment housings to complete dentures
Domingo, K.B. and Burgess, J.O. and Litaker, M.S. and McCracken, M.S.
Journal of Prosthetic Dentistry. 2013; 110(1): 8-13
[Pubmed]
3 Comprehensive Analysis of Repair/Reinforcement Materials for Polymethyl Methacrylate Denture Bases: Mechanical and Dimensional Stability Characteristics
R. Venkat,N. Gopichander,M. Vasantakumar
The Journal of Indian Prosthodontic Society. 2013; 13(4): 439
[Pubmed]
4 Strength comparison of four techniques to secure implant attachment housings to complete dentures
Karla B. Domingo,John O. Burgess,Mark S. Litaker,Michael S. McCracken
The Journal of Prosthetic Dentistry. 2013; 110(1): 8
[Pubmed]
5 Effect of repair resin type and surface treatment on the repair strength of heat-polymerized denture base resin
Murat Alkurt,Zeynep Yesil Duymus,Mustafa Gundogdu
The Journal of Prosthetic Dentistry. 2013;
[Pubmed]
6 Influence of surface treatments on the flexural strength of denture base repair
Rodrigo de Paula Pereira,Carina Sinclr Delfino,Luis Eduardo Butignon,Marcos Andr Kalabaide Vaz,Joo Neudenir Arioli-Filho
Gerodontology. 2012; 29(2): e234
[Pubmed]
7 Effects of aluminum oxide addition on the flexural strength, surface hardness, and roughness of heat-polymerized acrylic resin
Mahroo Vojdani,Rafat Bagheri,Amir Ali Reza Khaledi
Journal of Dental Sciences. 2012; 7(3): 238
[Pubmed]
8 Effects of aluminum oxide addition on the flexural strength, surface hardness, and roughness of heat-polymerized acrylic resin
Vojdani, M. and Bagheri, R. and Khaledi, A.A.R.
Journal of Dental Sciences. 2012; 7(3): 238-244
[Pubmed]
9 Influence of surface treatments on the flexural strength of denture base repair
De Paula Pereira, R. and Delfino, C.S. and Butignon, L.E. and Vaz, M.A.K. and Arioli-Filho, J.N.
Gerodontology. 2012; 29(2): e234-e238
[Pubmed]
10 Effect of thermal cycling on microleakage between hard chairside relines and denture base acrylic resins
Giampaolo, E.T. and Jorge, J.H. and MacHado, A.L. and Pavarina, A.C. and Vergani, C.E.
Gerodontology. 2011; 28(2): 121-126
[Pubmed]
11 Effect of thermal cycling on microleakage between hard chairside relines and denture base acrylic resins
Eunice Teresinha Giampaolo,Janaina Habib Jorge,Ana Lcia Machado,Ana Cludia Pavarina,Carlos Eduardo Vergani
Gerodontology. 2011; 28(2): 121
[Pubmed]
12 Flexural properties of repaired heat-polymerising acrylic resin after wetting with monomer and acetone
Canan Bural,Glsen Bayraktar,Ismail Aydin,Ibrahim Yusufoglu,Natuk Uyumaz,Mete Hanzade
Gerodontology. 2010; 27(3): 217
[Pubmed]
13 Flexural properties of repaired heat-polymerising acrylic resin after wetting with monomer and acetone
Bural, C. and Bayraktar, G. and Aydin, I. and Yusufòlu, I. and Uyumaz, N. and Hanzade, M.
Gerodontology. 2010; 27(3): 217-223
[Pubmed]



 

Top
 
 
  Search
 
 
 
    Similar in PUBMED
   Search Pubmed for
   Search in Google Scholar for
 Related articles
    Email Alert *
    Add to My List *
* Registration required (free)  
 


    Abstract
    Materials and Me...
    Results
    Discussion
    Conclusion
    References
    Article Tables

 Article Access Statistics
    Viewed4764    
    Printed142    
    Emailed1    
    PDF Downloaded1163    
    Comments [Add]    
    Cited by others 13    

Recommend this journal